Poly (Methyl Methacrylate) absorption and releasing of nystatin and fluconazole / Absorção e liberação de nistatina e fluconazol por polimetilmetacrilato

Objectives: The aim of this study was to verify if there are poly (methyl methacrylate) (PMMA) absorptionand releasing of nystatin (NYS) and fluconazole (FLZ) after simulated treatment of oral candidosis. Materialsand methods: Specimens (30 × 25 × 5 mm) prepared with PMMA polymerized by hot water bath or microwaveenergy were immersed into NYS (3.12 μg/mL), FLZ (2.56 μg/mL) or deionized water (control) during14 days at 35 ± 2 °C. After treatment simulation, specimens were immersed into distilled water during 3, 7, 10and 14 days. The immersion liquid was changed after each analysis. Higher performance liquid chromatographywas used in order to detect antifungal compounds. In order to determine if there was surface depositionof drugs on PMMA resin, specimens were analyzed with electronic microscopy (SEM). Results: None of theantifungal agents was released from the PMMA resins. Conclusion: Within the limitations of this study, itcould be concluded that PMMA resins had no drug absorption with posterior release.

Objetivos: O objetivo deste estudo foi verificar se o poli (metil metacrilato) (PMMA) é capaz de absorver e liberar nistatina (NYS) e fluconazol (FLZ) após simular um tratamento para candidose oral. Materiais e métodos:Espécimes (30 × 25 × 5 mm) foram preparados em resina de PMMA por banho de água quente ou energia demicro-ondas e, em seguida, imersos em solução contendo NYS (3.12 μg/mL), FLZ (2.56 μg/mL) ou água deionizada(controle) durante 14 dias a 35 ± 2 °C. Após a simulação de tratamento, os espécimes foram imersos em água destilada durante 3, 7, 10 e 14 dias. O líquido de imersão foi trocado após cada análise. Cromatografia líquida de alta performance foi utilizada para detectar a presença dos agentes antifúngicos. Para determinar se houve deposição dos agentes antifúngicos na superfície de PMMA, os espécimes foram analisados por microscopia eletrônica de varredura(MEV). Resultados: Não houve liberação de agentes antifúngicos dos espécimes. Conclusão: Considerando as limitações deste estudo, pode-se concluir que a resina de PMMA não absorve ou libera agentes antifúngicos.

Effect of spray volume on the moisture of stored corn and wheat grains

The goal of this work was to evaluate the effect of spray volume on the moisture of the stored grains of the corn and wheat. Two kg of each type of the grain were placed into the plastic bags and sprayed with the theoretical doses of 0, 1, 3, 5, 8, and 10 liters of water / ton of the grain. The grain moisture content was evaluated 24 h after the spray operation by the oven method. The increase in the grain moisture was quadratic and showed the same trend in both the corn and wheat. The grain moisture after spraying 10 L.t-1 showed little increase (0.8 percent) as compared to the initial moisture content. Thus, the application of any spray volume as used in this study made no difference for a possible better uniformity in the distribution of insecticide throughout the sprayed material.

A pulverização de inseticidas é o principal método de controle preventivo das pragas dos grãos armazenados. O objetivo deste trabalho foi avaliar o efeito do volume de pulverização na umidade de grãos de milho e trigo armazenados. Foram acondicionados 2 kg de grãos em sacos plásticos e pulverizados com doses teóricas de zero, 1, 3, 5, 8 e 10 litros de água / tonelada de grão. A avaliação do teor de umidade dos grãos foi feita 24 horas após a pulverização mediante o método da estufa. O acréscimo na umidade dos grãos em função do volume de água pulverizado, foi quadrático e teve a mesma tendência tanto para o milho como para o trigo. A umidade dos grãos após a pulverização de 10 L.t-1 teve pequeno acréscimo (0,8 por cento) quando comparado com o teor inicial. Desse modo, é indiferente o uso de qualquer volume estudado, visando a maior uniformidade de distribuição do inseticida na massa de grãos.